VENTURA ALLOY AND STEELS PRIVATE LIMITED
2714 Hot Work Tool Steel

2714 Hot Work Tool Steel

Send Inquiry

2714 Hot Work Tool Steel is an extreme pass on steel with high treating resistance and great through-solidifying properties. This evaluation is generally supplied in toughened condition or extinguished and tempered to 1300 N/mm² & a working hardness of 370 to 410 HB (round) or 355 to 400 HB (square, level).
Specifications:

Imported

Process:

EAF + LF + VD + Forged + Annealed + Oil QT (Quenched & Double Tempered)

Hardness

Below 245HB / 370 410 BHN

Diameter Tolerance

0/+3 mm max Blocks & 0/+2 mm max Rounds

Grain Size

6-8 acc to ASTM E 112-96

Ultra Standard

SEP: 1921, III D/d

Non Metallic Inclusion

2 max acc to ASTM E 45

Hardness Tolerance

2 HRC ( All material hardness in between 370 410 BHN)

Chemical Composition

C: 0.50 0.60, Mn: 0.65 0.95, P/S: 0.030 MAX, Si: 0.10 0.40, Cr: 1.0 1.20, V: 0.08 0.12, Mo: 0.45 0.55, Ni: 1.5 1.8

Tensile Strength

Corresponding to Hardness 1220 1390 N/mm2

Yield Strength

Corresponding to Tensile 1100 N/mm2 Minimum

Elongation

A% ->14%

Forging Ratio

5 : 1 Approx

Indian

Process

I/F + Forged + Annealed + OIL QT (Quenched & Double Tempered)

Hardness

Below 245 HB / 370 410 BHN

Diameter Tolerance

0/+10 mm max )But aim 5 mm)

Grain Size

6-8 acc to ASTM E112-96

Ultra Standard

SEP: 1921, III D/d

Non Metallic Inclusion

2 max acc to ASTM E 45

Hardness Tolerance

3 HRC ( All material hardness in between 370 410 BHN)

Chemical Composition

C: 0.50 0.60, Mn: 0.65 0.95, P/S: 0.030 MAX, Si: 0.10 0.40, Cr: 1.0 1.20, V: 0.08 0.12, Mo: 0.45 0.55, Ni: 1.5 1.8

Tensile Strength

Corresponding to Hardness 1220 1390 N/mm2

Yield Strength

Corresponding to Tensile 1100 N/mm2 Minimum

Elongation

A% ->14%

Forging Ratio

04:01:00